Abstract Objective This study aims to evaluate the effect of sonochemical treatment on the surface of yttria-stabilized tetragonal zirconia (Y-TZP) before and after the final sintering. Material and Methods Twenty-eight Y-TZP discs were divided into four groups (n=7), according to surface treatment: PRE: pre-sintering sonication with 30% nominal power for 15 min; POS: post-sintering sonication with 30% nominal power for 15 min; JAT: air abrasion with 50-μm alumina particles; and CON: control group with no treatment. The POS and JAT groups were sintered before sonication and the PRE group after sonication. Surface roughness was analyzed using confocal microscopy, after which resin cement cylinders were placed on the surface of the Y-TZP discs and subjected to mechanical microshear bond strength test until fracture. Surface roughness and microshear bond strength values underwent ANOVA and the Tukey tests. Results The surface roughness values for the PRE group (299.91 nm) and the POS group (291.23 nm) were not significantly different (p≥0.05), statistically, and the surface roughness value of the JAT group (925.21 nm) was higher than those of PRE and POS (p=0.007) groups. The mechanical microshear bond strength test showed that there was no statistically significant difference between the groups (p=0.08). Conclusions Therefore, the results showed that sonochemical treatment modifies the Y-TZP surface and is similar to the well-established sandblasting surface treatment regarding the strength of the bond with the resin cement.

<sec><title>Introduction</title><p> The Young Doctor Project (YDP) uses Telehealth and Interactive Teleducation instruments to promote the integration of different areas of health and to build knowledge. This methodology can also foster public awareness on various issues related to health. In this context, the objective of this study was to emphasize cleft lip and palate (CLP), which is one of the most common birth defects in Brazil.</p></sec><sec><title>Objective</title><p> The study aimed to apply a model of education regarding CLP, based on the dynamics of the YDP, and to evaluate the participants' knowledge acquired after participating in the YDP.</p></sec><sec><title>Methods</title><p> The participants were 41 students, 13 to 15 years of age and at the eight- and ninth-grade levels in a private elementary school in Bauru (Brazil). To analyze the performance of the participants, a questionnaire was administered before and after the completion of the training program. The training program was structured in three steps using: (1) interactive teleducation classes, (2) a cybertutor, and (3) practical activities.</p></sec><sec><title>Results</title><p> There was a statistically significant difference between the pre- and postparticipation questionnaire results. The improved performance of participants is evidenced by the increase in the rate of correct answers on all issues.</p></sec><sec><title>Conclusion</title><p> The YDP on CLP was applied in the school setting following the three steps recommended by the project, and, after the implementation of the training program, there was a significant increase in participants' knowledge of CLP. The YDP on CLP proved an effective tool in promoting health education.</p></sec>

OBJECTIVES: Calcium hydroxide cements have been largely used in deep cavities due to their abilities to stimulate dentin formation. However, their resistance can be relatively low and their solubility relatively high, in many instances. This study evaluated water sorption and solubility of different calcium hydroxide cements, in order to show alterations that may reduce their effectiveness. MATERIAL AND METHODS: Five discs (20 mm in diameter and 1.5 mm thick) of three different materials (Biocal®, Dycal® and Hidro C®) were prepared with the aid of a ring-shaped metallic matrix. After being stored at 37ºC for 24 h, the discs were weighed on a precision weight scale, dehydrated and weighed again. Immediately after weighing, discs were stored for a week in 50 mL of distilled water at 37ºC and, then, weighed again, dehydrated and submitted to a new weighing. The loss of soluble material and its water sorption was obtained from the difference between the initial and the final dry mass of each disc, after 1 week of immersion in water. Data were analyzed for significant differences by two-way ANOVA and Tukey's test (p<0.05). RESULTS: Mean water sorption values (g) ± standard deviation and percentage (%), for each evaluated cement, were: Biocal® (0.006 ± 0.001 / 2.15); Dycal® (0.016 ± 0.004 / 5.49); and Hidro C® (0.025 ± 0.003 / 8.27). Mean solubility values (g) ± standard deviation and percentage (%), for each evaluated cement, were: Biocal® (0.002 ± 0.001 / 0.72); Dycal® (0.013 ± 0.004 / 4.21); and Hidro C® (0.023 ± 0.004 / 7.65). CONCLUSIONS: Biocal® absorbed less water and was less soluble than the other evaluated cements; Hidro C® exhibited the highest water sorption and solubility values; and there were significant differences among all evaluated experimental groups.

Glass ionomer based materials are clinically popular in several areas of restorative dentistry, but restoration of cervical lesions has proven particularly successful. Various etiologies, conformations, locations and structural characteristics make non-carious cervical lesions more challenging to adhesive restorative procedures and marginal seal in the long run. Due to their characteristics, glass ionomer cements (GICs) have precise indication for these cases. Moreover, the use of a GIC base underneath composite resin, the so-called "sandwich" or mixed technique, allows associating the good characteristics of composite resins and GICs, and has been considered quite useful in the restoration of non-carious cervical defects. The aim of this paper is to critically review the literature and discuss peculiar features of GICs regarding their role in the restoration of non-carious cervical lesions.

OBJETIVO: testar se existe alteração na resistência adesiva de dois cimentos utilizados na colagem de acessórios ortodônticos ao esmalte dentário bovino, sendo um de polimerização química (Concise ortodôntico) e outro fotopolimerizável (Transbond XT), após a aplicação de cargas contínuas. METODOLOGIA: foram utilizados para este estudo 80 dentes bovinos e 80 braquetes metálicos. O esmalte bovino foi condicionado com ácido fosfórico a 37% por 1 minuto e depois lavado e seco. A aplicação dos adesivos, manipulação e aplicação dos dois cimentos foram feitas de acordo com as instruções dos fabricantes. Após 24 horas, todos os braquetes foram submetidos a cargas contínuas de 30g, 70g e 120g, menos o grupo controle, que não recebeu carga alguma. Os espécimes ficaram imersos em água filtrada por 28 dias dentro de uma estufa a 37°C. Depois deste período, as amostras foram submetidas a testes de cisalhamento em uma Máquina de Ensaios Universal Kratos. Os resultados foram registrados e enviados para análise estatística. CONCLUSÕES: (1) o cimento Concise apresentou maior resistência à remoção que o cimento Transbond XT para todas as cargas utilizadas, (2) não houve diferença estatisticamente significante na resistência adesiva frente às três cargas utilizadas para os dois cimentos testados; (3) no momento da fratura, conforme ocorreu o aumento da carga, a porcentagem de fratura do esmalte diminuiu para o Concise, ao contrário do cimento Transbond XT, onde a porcentagem de fratura de esmalte se manteve constante com o aumento das cargas.

AIM: The purpose of this study was to test differences on bond strength between auto-cured (Concise) and light-cured (Transbond XT) cements after static loading and shear test. METHODS: Eighty bovine teeth and metallic orthodontic brackets (Morelli Ortodontia Braquete Edgewise/Rickets) were tested after static loads of 30, 70 and 120grs. Bovine enamel was conditioned with 37% phosphoric acid gel for one minute, rinsed and dried. Adhesives were applied and brackets were bonded according to manufacturer’s instructions. Cement thickness was standardized with the use of a heavier Gilmore needle. After 24 hours, half of the specimens were submitted to the static loads of 30, 70 and 120grs. Control group remained unloaded. Then, specimens were immersed in distilled water for 28 days at 37ºC. Afterwards, orthodontic brackets were attached to a loop wire and submitted to a shear force (Máquina de Ensaios Kratos Universal Kratos) under a crosshead speed of 0.5mm/min and load cell of 500Kgf. A two-way ANOVA test (alpha = 0.05) was used to detect significant interactions between cements and static loads. CONCLUSIONS: (1) The Concise cement showed more statistically significant bond strength values than the Transbond XT cement for all static loads; (2) No statistically significant differences were observed regarding static loads for all cements tested and (3) Higher static loads provided less enamel fracture in the Concise group after shear test, whereas in the Transbond XT the rate of enamel fracture remained unchanged regardless of previous load applied.

The polymerization shrinkage of composite resins may affect negatively the clinical outcome of the restoration. Extensive research has been carried out to develop new formulations of composite resins in order to provide good handling characteristics and some dimensional stability during polymerization. The purpose of this study was to analyze, in vitro, the magnitude of the volumetric polymerization shrinkage of 7 contemporary composite resins (Definite, Suprafill, SureFil, Filtek Z250, Fill Magic, Alert, and Solitaire) to determine whether there are differences among these materials. The tests were conducted with precision of 0.1 mg. The volumetric shrinkage was measured by hydrostatic weighing before and after polymerization and calculated by known mathematical equations. One-way ANOVA (<FONT FACE=Symbol>a</font > or = 0.05) was used to determine statistically significant differences in volumetric shrinkage among the tested composite resins. Suprafill (1.87±0.01) and Definite (1.89±0.01) shrank significantly less than the other composite resins. SureFil (2.01±0.06), Filtek Z250 (1.99±0.03), and Fill Magic (2.02±0.02) presented intermediate levels of polymerization shrinkage. Alert and Solitaire presented the highest degree of polymerization shrinkage. Knowing the polymerization shrinkage rates of the commercially available composite resins, the dentist would be able to choose between using composite resins with lower polymerization shrinkage rates or adopting technical or operational procedures to minimize the adverse effects deriving from resin contraction during light-activation.

Para avaliar o efeito de diferentes tratamentos superficiais sobre a resistência ao cisalhamento da união entre uma liga metálica (Co-Cr-Mo - Remanium CD) e um cimento resinoso (Rely X TM) e analisar o tipo de fratura durante a separação dos espécimes, quarenta pares de discos metálicos foram fundidos, regularizados e polidos, submetidos a quatro ciclos térmicos (vácuo, 960ºC, 8 minutos) e divididos aleatoriamente em quatro grupos. Cada grupo recebeu um tipo de tratamento: Grupo PSP: Polimento com lixa d'água Nº 600; Grupo PCP: Polimento com lixa 600 e aplicação do condicionador metálico Alloy Primer (Kuraray); Grupo JSP: Jato de óxido de alumínio de 100µm, e Grupo JCP: Jato de óxido de alumínio de 100mm, e aplicação do Alloy Primer. Os grupos foram cimentados e armazenados em água destilada a 37ºC por 36 horas e submetidos ao ensaio de resistência ao cisalhamento. A média e o desvio padrão (em kgf/cm²) obtidos para cada grupo foram: PSP 4,0/0,4; PCP 88,9/33,6; JSP 163,2/27,6; JCP 144,5/54,0. Após a análise estatística os autores concluíram que: os maiores valores foram produzidos pelos grupos jateados (JSP, JCP), independentemente da aplicação do primer; o Alloy Primer aumentou a retentividade entre o cimento Rely X e a superfície polida da liga de Co-Cr-Mo, entretanto sua força de união não superou a alcançada através do jateamento; todos os espécimes apresentaram falha adesiva na interface testada.

To evaluate the effect of different surface treatments on shear bond strength between a metallic alloy (Co-Cr-Mo - Remanium CD) and a resin cement (Rely X TM) and to evaluate the mode of fracture after testing, forty couples of metallic-alloy disks were melted, regularized, polished, submitted to four thermal cycles (Vacuum, 960ºC, 8 minutes) and randomly separated into four groups. Each group received a different type of treatment: Group PSP: Polished with sandpaper 600; Group PCP: Polished with sandpaper 600 and application of the metal primer Alloy Primer (Kuraray); Group JSP: Sandblasted with 100µm aluminum oxide; Group JCP: Sandblasted with 100mm aluminum oxide and treated with a metal Primer. The groups were cemented and stored in distilled water at 37ºC for 36 hours and submitted to the shear bond strength test. The mean and standard deviation (in Kgf/cm²) obtained for each group was: PSP 4.0/0.4; PCP 88.9/33.6; JSP 163.2/27.6; JCP 144.5/54.0. After the statistical analysis the authors concluded that: the highest values were obtained for the sandblasted groups (JSP, JCP), regardless of the primer application; the Alloy Primer increased the retention between the Rely X cement and the polished surface of the Co-Cr-Mo alloy, yet its bond strength was not greater than that obtained with sandblasting; all specimens showed adhesive failures in the tested interface.

Avaliou-se a resistência à tração diametral e a sorção de água de cimentos de ionômero de vidro restauradores (Fuji IX e Ketac Molar) e modificados por resina indicados para cimentação (ProTec Cem, Fuji Plus e Vitremer) manipulados na proporção pó: líquido indicada pelo fabricante e em maior proporção para a utilização no Tratamento Restaurador Atraumático. O ionômero restaurador convencional (Ketac Fil) foi utilizado como controle. Espécimes (6,0 mm de diâmetro x 3,0 mm de altura) foram preparados e armazenados (1 hora, 1 dia e 1 semana) para o teste de resistência à tração diametral. Os dados foram submetidos a ANOVA a dois critérios e ao teste de Tukey (p<0,05). Para o teste de sorção de água, espécimes com 15,0 mm de diâmetro x 0,5 mm de altura foram preparados e transferidos a dessecadores até a obtenção de uma massa constante. Em seguida, os espécimes foram imersos em água deionizada por 7 dias, pesados e recondicionados a uma massa constante em dessecadores. Os dados foram submetidos a ANOVA a um critério e ao teste de Tukey (p<0,05). Cinco espécimes de cada material e consistência foram preparados para cada teste. Os ionômeros modificados por resina mostraram maior resistência que os convencionais. Exceto pelo ProTec Cem, a resistência dos materiais modificados por resina significativamente aumentou da consistência cimentante para a restauradora. Exceto pelo ProTec Cem, a sorção de água dos ionômeros modificados por resina foi maior que a dos outros ionômeros. A sorção de água dos materiais modificados por resina na consistência restauradora foi significativamente menor que na consistência de cimentação. Os cimentos de ionômero de vidro modificados por resina indicados para cimentação manipulados em maior proporção pó: líquido apresentaram melhores propriedades que na consistência de cimentação.

The purposes of this study were to evaluate the diametral tensile strength and the water sorption of restorative (Fuji IX and Ketac Molar) and resin-modified glass-ionomer luting cements (ProTec Cem, Fuji Plus and Vitremer) mixed at both manufacturer and increased powder: liquid ratio, for their use in the Atraumatic Restorative Treatment. A conventional restorative glass-ionomer (Ketac Fil) was used as control. Specimens (6.0 mm in diameter x 3.0 mm in height) were prepared and stored (1 hour, 1 day and 1 week) for a diametral tensile strength test. Data were subjected to two-way ANOVA and Tukey tests (p<0.05). For the water sorption test, specimens of 15.0 mm in diameter x 0.5 mm in height were prepared and transfered to desiccators until a constant mass was obtained. Then the specimens were immersed in deionized water for 7 days, weighed and reconditioned to a constant mass in desiccators. Data were subjected to one-way ANOVA and Tukey tests (p<0.05). Five specimens of each studied material and consistency were prepared for each test. The resin-modified glass-ionomer cements showed significantly higher strength than the conventional materials. Except for ProTec Cem, the diametral tensile strength of the resin-modified materials significantly increased from luting to restorative consistency. Except for ProTec Cem, the water sorption of the resin-modified glass ionomers was higher than the others. The water sorption of resin-modified materials at restorative consistency was significantly lower than at luting consistency. Resin-modified glass-ionomer luting cements mixed at increased powder: liquid ratio showed better properties than at luting consistency.